中文摘要: 冲刷速度是影响飞灰冲蚀磨损的主要因素,速度对冲蚀磨损的影响与温度有着很大的关系.研究了12Cr1MoV合金钢在不同温度时冲刷速度对磨损率的影响,并且用速度指数n表征.试验数据结果表明:在热态试验中(250~550 ℃),飞灰磨损速度指数为1.006 27~0.827 52;而在常温态试验中,速度指数达到2.95,基本规律为飞灰磨损速度指数随温度的升高而降低,且常温态的相对磨损率明显大于热态时的相对磨损率.
中文关键词: 电厂锅炉 冲蚀磨损机理 速度指数 12Cr1MoV合金钢
Abstract:The velocity is the major effective factor for the flying-ash erosion,and its influence has close relation with the temperature condition.The influence of particle velocity for flying-ash erosion of 12Cr1MoV steel is studied on the experiment,in different temperature conditions,and is characterized by velocity index.The analysis on the data of the flying-ash erosion tests shows that the velocity index for flying-ash erosion varies from 1.006 27 to 0.827 52 in hot conditions from 250 ℃ to 550 ℃,and 2.95 at normal atmosphere temperature.So the basic rule is that the velocity index for flying-ash erosion varies as the inverse temperature and the relative erosion-wear is significantly higher at normal atmosphere temperature than that in hot conditions.
文章编号：20160101 中图分类号： 文献标志码：
基金项目:上海市地方能力建设项目(13160501000).
| 作者 | 单位 | |
| 赵宪萍 | 上海电力学院 能源与机械工程学院 | zhaoxianping@shiep.edu.cn |
| 叶桂林 | 上海电力学院 能源与机械工程学院 | |
| 朱崇武 | 上海电力学院 能源与机械工程学院 | |
| 孙坚荣 | 上海电力学院 能源与机械工程学院 |
引用文本：
赵宪萍,叶桂林,朱崇武,等.不同温度工况下飞灰磨损速度指数特性的试验研究[J].上海电力大学学报,2016,32(1):1-4,24.
ZHAO Xianping,YE Guilin,ZHU Chongwu,et al.Experimental Study on the Characteristic of Velocity Index for Flying-ash Erosion at Different Temperature Conditions[J].Journal of Shanghai University of Electric Power,2016,32(1):1-4,24.
赵宪萍,叶桂林,朱崇武,等.不同温度工况下飞灰磨损速度指数特性的试验研究[J].上海电力大学学报,2016,32(1):1-4,24.
ZHAO Xianping,YE Guilin,ZHU Chongwu,et al.Experimental Study on the Characteristic of Velocity Index for Flying-ash Erosion at Different Temperature Conditions[J].Journal of Shanghai University of Electric Power,2016,32(1):1-4,24.