中文摘要: 以脂肪酸(己酸、辛酸、癸酸)和N,N-二甲基乙醇胺为原料,合成了3种醇胺酯类阻锈剂HMEA,OMEA,CMEA.电化学分析结果表明:3种阻锈剂通过物理、化学吸附作用在钢筋表面形成了保护层,有效地抑制了试样在模拟孔隙液中的腐蚀反应.其中OMEA的效果最为显著,浓度为0.4%时,其缓蚀效率达到66.4%,对混凝土无不良影响,具有良好的应用前景.
Abstract:Three kinds of organic inhibitors (HMEA,OMEA,CMEA) are synthesized using fatty acid (hexylic acid,octanoic acid,capric acid) and N,N-dimethyl ethanolamine as raw materials.Electrochemical analytical result shows that the formation of organic film on iron through chemical or physical adsorption is the main cause of preventing the corrosion reaction effectively.Among the three inhibitors,OMEA proves more effective when its content is 0.4%(percent weight relative to simulated concrete solution),the corrosion inhibition rate is up to 66.4% compared with blank specimen.Having no harmful effect to the concrete,it has application prospect.
文章编号：20140212 中图分类号： 文献标志码：
基金项目:上海市基础研究重点项目(09JC1406800,11JC1404400).
| 作者 | 单位 | |
| 高立新 | 上海电力学院环境与化学工程学院 | glx2010@shiep.edu.cn |
| 张大全 | 上海电力学院环境与化学工程学院 | |
| 李光勇 | 河南省医药技师学院制药工程系 | |
| 谢亚东 | 上海电力学院环境与化学工程学院 | |
| 曾琛翔 | 上海电力学院环境与化学工程学院 | |
| 权德贤 | 上海电力学院环境与化学工程学院 | |
| 鲍煜 | 上海电力学院环境与化学工程学院 |
引用文本：
高立新,张大全,李光勇,等.醇胺酯类阻锈剂对混凝土钢筋的保护作用[J].上海电力大学学报,2014,30(2):149-154.
GAO Lixin,ZHANG Daquan,LI Guangyong,et al.The Performance of Alcohol Amine Ester Corrosion Inhibitor for Steel in Concrete[J].Journal of Shanghai University of Electric Power,2014,30(2):149-154.
高立新,张大全,李光勇,等.醇胺酯类阻锈剂对混凝土钢筋的保护作用[J].上海电力大学学报,2014,30(2):149-154.
GAO Lixin,ZHANG Daquan,LI Guangyong,et al.The Performance of Alcohol Amine Ester Corrosion Inhibitor for Steel in Concrete[J].Journal of Shanghai University of Electric Power,2014,30(2):149-154.